The main raw materials for the production of mullite sillimanite bricks are synthetic mullite and sillimanite materials, which are obtained by high-temperature sintering. The product is divided into two grades: MG-65, MG-70, and MG-65 with Al2O3 65% and MG-70 with Al2O3 70%. The Fe2O3 content of the product is low, ranging from 0.8% to 1.0%, with high compressive strength above 1600 ℃, low rate of change in the firing line, 1500 ℃ * 2h 0~+0.5%, good thermal shock stability, and water cooling at 1100 ℃>20 korda. Toote kõige olulisem omadus on tugev kulumiskindlus ja vastupidavus süsiniku sadestumisele. Seda kasutatakse peamiselt kõrgahjude šahtide ja muude kõrge temperatuuriga tööstuslike ahjude ülemises ja keskmises osas, et tagada vastupidavus kiirele jahutamisele ja kuumutamisele, kulumiskindlusele ja muudele aladele.